Influence of Silicon Oxynitride on Slag Resistance of Al2O3-SiC-C Refractory

doi:10.19691/j.cnki.1004-4493.2019.01.007

• Original article • Previous Articles Next Articles

Influence of Silicon Oxynitride on Slag Resistance of Al2O3-SiC-C Refractory

ZHANG Guotan, LI Chenchen, LIANG Yonghe, WANG Wei

Published:2019-07-02

Abstract

Abstract: Silicon oxynitride was added in shaped Al2O3-SiC-C refractory material to improve the slag resistance in this paper. Optimum adding quantity of silicon oxynitride powder was also studied. The results show that the slag resistance of Al2O3-SiC-C shaped refractory is improved when 2% or 3% Si2N2O is added. A reasonable amount of Si2N2O added into Al2O3-SiC-C shaped refractory can produce silicon oxide into the slag, which can improve the viscosity of slag and prevent the slag erosion and penetration.

Key words: slag resistance, silicon oxynitride, alumina-silicon carbide-carbon shaped refractory

ZHANG Guotan, LI Chenchen, LIANG Yonghe, WANG Wei. Influence of Silicon Oxynitride on Slag Resistance of Al2O3-SiC-C Refractory[J]. , DOI: 10.19691/j.cnki.1004-4493.2019.01.007.

[1]	CAO Zhuang, JIA Qingwei, ZHANG Jun, ZHOU Huijun, LI Jinfeng, HUN Xianlei, YAN Leixin, QIN Hongbin, ZHANG Sanhua. Effect of Different Silica Fumes on Properties of Al₂O₃-SiC-C Castables for Iron Trough [J]. China's Refractories, 2023, 32(2): 31-36.
[2]	Ao HUANG, Shenghao LI, Yongshun ZHOU, Huazhi GU, Guangqiang LI, Yawei LI. Research Progress on Slag Resistance of Refractories with Electromagnetic Field [J]. China's Refractories, 2020, 29(3): 19-23.
[3]	CHEN Wei, ZHANG Xiaohui, ZHANG Haijun. Slag Resistance of Refractories for Direct Reduction of Laterite Nickel Ores in Rotary Kilns [J]. China's Refractories, 2020, 29(2): 11-20.
[4]	TIAN Xuekun, CHEN Anbang, LI Na, LIAO Guihua, DING Dafei, YE Guotian. Effect of Andalusite Aggregate Pre-fired at Different Temperatures on Properties of Al2O3-SiC-C Castables [J]. , 2019, 28(2): 41-45.
[5]	SHEN Mingke, WEI Guoping, XUE Junzhu, HE Bo. Effect of SiO2 Micropowder Addition on Properties of Alumina-magnesia Based Wet Gunning Mix for Working Layer [J]. , 2017, 26(4): 12-16.
[6]	LI Zhigang, YE Fangbao. Effect of Nano Calcium Carbonate on Properties of Corundum-spinel Castables [J]. , 2013, 22(4): 9-13.
[7]	ZHANG Qiaoyan, ZHU Boquan, LI Xiangcheng. Corrosion Behavior of Slags with Different Basicities to Alumina Magnesia Castables [J]. , 2012, 21(4): 17-21.
[8]	ZHANG Daoyun,JIANG Mingxue,XIAO Guoqing, HUANG Shaobo. Influence of Nano-Al2O3 on Properties of Magnesia Chrome Refractories [J]. China's Refractories, 2012, 21(2): -.
[9]	YIN Guoxiang, PAN Bo, GAO Xinkui. Corrosion Resistance Mechanism of Magnesia Zirconia Brick to [J]. China's Refractories, 2011, 20(3): -.
[10]	CHEN Zhaoyou. Refractories for RH Degassers and Ways of Improving Their Lining Life [J]. China's Refractories, 2010, 19(2): -.
[11]	PENG Conghua, LI Nan, HAN Bingqiang. Influence of Microporous Magnesia-rich Spinel Aggregates on Properties of Low Carbon MgO-C Refractories [J]. China's Refractories, 2010, 19(1): -.
[12]	YU Renhong, AO Ping, ZHOU Ningsheng. Influence of SiC Contents in Al2O3-SiO2 Castableson Resistance to PbO rich Slag [J]. China's Refractories, 2009, 18(3): -.
[13]	CHEN Junhong, ZHAN Huasheng, XIE Jing. High temperature Reaction of Silica Fume-Si3N4 System [J]. China's Refractories, 2009, 18(3): -.
[14]	SHI Huiying, ZHANG Yang, BU Xiangjuan. Effect of Treated Graphite on Properties of Al2O3-SiC-C Castables [J]. China's Refractories, 2009, 18(2): -.
[15]	GU Huazhi, WANG Houzhi, XUE Haitao. Slag Resistance of Magnesite-chrome Brick Impregnated with Chrome-bearing Sols [J]. China's Refractories, 2009, 18(1): -.

China's Refractories

Influence of Silicon Oxynitride on Slag Resistance of Al2O3-SiC-C Refractory

PDF

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments